Create colorful world
NEITABOND embossed aluminum composite panel is made by embossed aluminum coil with high anti-scratch characteristics, it shows various finishing on the surface and make a good choice for the designers.
NEITABOND embossed aluminum composite panel is a special coating ACP.
It is came out after embossed pattern formed on the surface of a variety of aluminum products, its usage is wide, mainly used in packaging, roof, truck body construction , walls, and so on.
Soft white or bright red? Solid colours are always a good choice when a uniform appearance without special effects is required.
1.Good anti-abrasion
2.High anti-scratch
3.Excellent weatherproof durability
4.Anti-ultraviolet
5.High erosion resistance
6.Good mechanical processing performance
7.Anti-impact
8.High flexibility
| Aluminum alloy | AA1100 H 18 |
| Aluminum skin | 0.21mm,0.30mm,0.40mm,0.5mm |
| Panel thickness | 2mm,3mm,4mm,5mm,6mm |
| Panel width | 1220mm,1250mm,1500mm |
| Panel length | 2440mm,3050mm,4050mm |
| Surface treatment | Polyester |
| Colors | RAL COLORS |
| Customers size | accepted |
| GLOSSY | 20%-50% |
Panel width: ±2mm
Panel length:±3mm
Panel thickness: ±0.2mm
Panel diagonal: ≤5mm
Aluminum sheet thickness: ±0.02mm
| Description | Test standard | Polyester |
| Thickness of coating | Polyester paint ≥16um | 16um to 18um |
| Coating flexibility (T-bend) | Polyester paint≥3T | 3T |
| Color different | ΔE≤2.0(follow color sample) | ΔE≤2.0 |
| Pencil hardness | ≥HB | ≥2H |
| Chemical resistance | 2%HCI or 2%NaOH test in 24 hours -No change | No change |
| Coating adhesion | ≥1grade for 10810mm2gridding test | 1grade |
| Resist solvent | 100times with Dimethylebnzene without change | No change |
| Boiling water resistance | 2 hours without change | No change |
Peeling strength/ stripping strength | Average ≥5N/mm of 180oc peel off for panel with 0.21mm alu.skin | 5N/mm |
| Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40℃ to +80℃ temperature without change of color difference andpaint peel off, peeling strength average dropprate≤10% | Change of glossy only,no paint |
| Peel off | ||
Cofficient of linear Thermal Expansion | 100℃ temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition ,glossiness deviation less grade 2,color difference ≤4.0 | No change |
The company possesses production lines for aluminum-plastic panels whose annual output is 520 million square meters.
Address：Zhongwei Road, Zhubao Industrial Zone, Lanshan District, Linyi City,Shandong China
E-mail：sales@neitabond.com
Tel：+86-539-3595209
Fax：+86-539-359520
Cell：+86-13583916866
Espacio Riesco, Santiago, ChileBOOTH
30th Jul.2019EXHIBITION: SIGN CHINA 2019 • SHANGHAI
29th Jul.2019EXHIBITION:THE 26TH SHANGHAI INT'LAD &SIGN TECHNOLOGY&EQUIPMENT EXHIBITION
01st Mar.2018
Linyi city Xingda Plastic Decoration Material Co.,Ltd. All Rights Reserved. Powered by HiCheng