NEITABOND High glossy aluminum composite panel is a new composite material skinned with anodized high glossy aluminum sheets. The lower aluminum skin is chromate treated and polyester coated. It is available in a 3mm 4mm thickness with a choice of 0.5mm skin or 0.4mm or 0.3mm skin and 1220mm,1250mm,1500mm widths.
NEITABOND Glossy coating, with polyurethane as base and fluoride polymer as top coating, has good feature of weather resistance of 10 years for interiors use. Different from PE coating, it guarantees fresher, vivid color and higher gloss level, provide more choice for designer. It is available in colors that are not feasible with other coating system.
Soft white or bright red? Solid colours are always a good choice when a uniform appearance without special effects is required.
High resistance to peeling
Superior weather resistance
Light weight and easy to process
Coating evenness
Diversified colors
Easy for maintenance
Impact resistance
| Aluminum | AA1100 AA3003 |
| Aluminum skin | 0.21mm,0.30mm,0.35mm,0.40mm,0.45mm,0.5mm |
| Panel thickness | 3mm,4mm,5mm,6mm |
| Panel width | 1220mm,1250mm,1500mm |
| Panel length | 2440mm,3050mm,4050mm |
| Surface treatment | Glossy PE |
| Colors | 70 colors, special colors available upon request |
| Customers size | accepted |
| Glossy | 20%-80% |
Panel width: ±2mm
Panel length:±3mm
Panel thickness: ±0.2mm
Panel diagonal: ≤5mm
Aluminum sheet thickness: ±0.02mm
| Description | Test standard | Polyester |
| Thickness of coating | Polyester paint >=16um | 16um to 18um |
| Coating flexibility (T-bend) | Polyester paint≥3T | 3T |
| Color different | ΔE≦2.0(follow color sample) | ΔE≦2.0 |
| Pencil hardness | ≧HB | ≧2H |
| Chemical resistance | 2%HCI or 2%NaOH test in 24 hours -No change | No change |
| Coating adhesion | ≧1grade for 10810mm2gridding test | 1grade |
| Resist solvent | 100times with Dimethylebnzene without change | No change |
| Boiling water resistance | 2 hours without change | No change |
| Peeling strength/stripping strength | Average ≧5N/mm of 180oc peel offfor panel with 0.21mm alu.skin | 5N/mm |
| Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40℃ to +80℃ temperature without change of color difference and paint peel off,peeling strength average dropprate≦10% | Change of glossy only,no paint |
| Peel off | ||
| Cofficient of linear Thermal Expansion | 100℃ temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
| Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
| Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference ≦4.0 | No change |
The company possesses production lines for aluminum-plastic panels whose annual output is 520 million square meters.
Address：Zhongwei Road, Zhubao Industrial Zone, Lanshan District, Linyi City,Shandong China
E-mail：sales@neitabond.com
Tel：+86-539-3595209
Fax：+86-539-359520
Cell：+86-13583916866
Espacio Riesco, Santiago, ChileBOOTH
30th Jul.2019EXHIBITION: SIGN CHINA 2019 • SHANGHAI
29th Jul.2019EXHIBITION:THE 26TH SHANGHAI INT'LAD &SIGN TECHNOLOGY&EQUIPMENT EXHIBITION
01st Mar.2018
Linyi city Xingda Plastic Decoration Material Co.,Ltd. All Rights Reserved. Powered by HiCheng